    題名: Miscibility and flexibility of poly (lactic acid) blends with octadecenylsuccinic anhydride
    作者: Don, Trong-Ming;Li, Ting-Shu;Lai, Wei-Chi
    關鍵詞: Poly(lactic acid);Octadecenylsuccinic anhydride;Miscibility;Flexibility
    日期: 2019-04
    上傳時間: 2019-09-11 12:10:19 (UTC+8)
    出版者: ELSEVIER
    摘要: Poly(lactic acid) (PLA) is the most used biodegradable polymer derived from renewable resources. However, PLA is a brittle plastic with low resistance to fracture. In this study, we tried to increase flexibility and hydrophobicity by melt-blending it with octadecenylsuccinic anhydride (ODSA) which was synthesized by reaction of octadecene and maleic anhydride. After mixing, thermal and mechanical properties of the PLA/ODSA blends (100/5, 100/10, 100/15) were measured. The results showed that at low contents of ODSA, the PLA was miscible with ODSA, and the PLA/ODSA blends had higher hydrophobicity than the neat PLA. The water contact angle of the PLA/ODSA (100/15) reached a value of 95.9°. Moreover, The addition of ODSA decreased the glass transition temperature and crystallization temperature, producing most α′ crystals during crystallization and therefore resulting in the observed exotherm in DSC curves owing to the α′-to-α crystal transformation. Most importantly, the flexibility was improved as the elongation at break increased from 3.1% for the PLA to 15.1% for the PLA/ODSA blend (100/10), in which stress-whitening was observed during tensile testing. The biodegradability of the PLA/ODSA blends was tested using proteinase K, and the results showed the addition of ODSA did not affect the enzymatic degradability of the PLA.
    關聯: Polymer degradation and stability 162, p.55-65
    DOI: 10.1016/j.polymdegradstab.2019.01.035
    顯示於類別:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML130檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋