    题名: 使用以靜電力場輔助電鍍法製備具微米構形聚二氧乙基噻吩 : 鉑複合薄膜光電致色變元件之製作與性質分析
    其它题名: Fabrication and characterization of photoelectrochromic devices using micropatterned poly(3,4-ethylenedioxythiophene) : platinum composited thin films prepared by electrostatic field-assisted electrodeposition
    作者: 鄭宗麟;Cheng, Tzung-Lin
    贡献者: 淡江大學化學工程與材料工程學系碩士班
    林正嵐
    关键词: 光電致色變元件;聚二氧乙基噻吩;Photoelectrochromic Devices;Poly(3,4-ethylenedioxythiophene);3,4-ethylenedioxythiophene
    日期: 2017
    上传时间: 2018-08-03 14:59:12 (UTC+8)
    摘要: 本研究以靜電力場輔助電鍍法製備具微米構形聚二氧乙基噻吩-鉑複合薄膜光電致色變元件之製作與性質分析，實驗分為兩部分。
    Part 1：以靜電力場輔助電鍍法製備聚二氧乙基噻吩(PEDOT)和鉑複合薄膜，並且改變PEDOT不同析鍍電量參數(15 ~ 35 mC/cm2,mPEDOT Q15 ~ Q35)，對薄膜以光學顯微鏡、循環伏安法、計時安培法及紫外線可見光光譜分析其表面、電致色變和光學性質。由紫外線可見光光譜與電化學測試發現穿透率調幅(delta T)與著色效率(C.E.)以mPEDOT Q25效果最好。再以脈衝電沉積鉑製備出聚二氧乙基噻吩-鉑複合薄膜，藉由改變電鍍的先後順序，製備出mPEDOT、Pt-mPEDOT (先沉積PEDOT)和mPEDOT-Pt (先沉積鉑)薄膜，發現電致色變的應答時間為mPEDOT-Pt < mPEDOT< Pt-mPEDOT。
    Part 2 : 以微米構形聚二氧乙基噻吩-鉑複合薄膜作為光電致色變元件(photoelectrochromic device, PECD)工作電極，對電極用15 wt% P25漿料以旋轉塗佈方式塗佈，再以450℃鍛燒。PECD閉環狀態經由紫外燈照光(365 nm, 5 mW/cm2)一分鐘著色，再以關燈閉環或開環去色觀察元件照光應答時間，以微米構形的聚二氧乙基噻吩-鉑複合薄膜的PECD去色應答時間優於聚二氧乙基噻吩的PECD，表示鉑助於電解質中氧化還原對I3-再生還原成I-過程，使去色應答時間縮短。
    In this study, the fabrication and characterization of photoelectrochromic devices with micropattern poly(3,4-ethylenedioxythiophene)-platinum composite thin films prepared by electrostatic field-assisted electrodeposition were studied. The experiment was divided into two parts. Part 1 : Micropattern poly(3,4-ethylenedioxythiophene)-platinum composite thin films were prepared by electrostatic field-assisted electrodeposition. The different electrodeposition charge parameters (15 ~ 35 mC / cm2, mPEDOT Q15 ~ Q35) of the thin films were studied. The films were characterized by optical microscopy (OM), cyclic voltammetry (CV), chronoamperometry (CA) and ultraviolet/visible (UV/Vis) spectroscopy to analyze their surface structure, electrochromism and optical properties. UV/Vis spectrum and electrochemical tests showed that mPEDOT Q25 had the best effect on transmittance modulate (
    显示于类别:[化學工程與材料工程學系暨研究所] 學位論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML145检视/开启

    在機構典藏中所有的数据项都受到原著作权保护.

    TAIR相关文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回馈