Effect of a low-molecular-weight compatibilizer on the immiscible blends of cellulose acetate propionate and poly(butylene terephthalate)

doi:10.1007/s10965-018-1487-5

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/113024

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/113024

题名:	Effect of a low-molecular-weight compatibilizer on the immiscible blends of cellulose acetate propionate and poly(butylene terephthalate)
作者:	Nai-Yun Liang;Trong-Ming Don;Chih-Yuan Huang;Chia-Fen Lee;Wen-Yen Chiu
关键词:	Cellulose acetate propionate (CAP);Poly(butylene terephthalate) (PBT);Compatibilizer Partially miscible;Nanofiber
日期:	2018-04
上传时间:	2018-03-29 12:11:10 (UTC+8)
出版者:	Springer Netherlands
摘要:	Blends of poly(butylene terephthalate) (PBT) and cellulose acetate propionate (CAP) were found to be immiscible. In order to improve the interfacial strength and miscibility of the PBT/CAP blends, a low-molecular-weight poly(ethylene glycol) (PEG) was thus pre-mixed with the CAP to form the P-CAP mixture. It was then blended with the PBT up to 15 wt% using a twin-screw extruder to prepare the PBT/P-CAP blends, and subsequently processed into the films and fibers by compression-molding and melt-spinning, respectively. The thermal and dynamic mechanical analyses suggested that the PBT and CAP became partially miscible and the interfacial strength was thus improved in the PBT/P-CAP blends, owing to the addition of PEG. The PEG was not only miscible with the CAP but also with the PBT, and it served as a plasticizer as well as a compatibilizer. From the observation of the fractured surface of the PBT/P-CAP films, the PBT component was present as dispersed particles in the P-CAP matrix with size ranging from 1.4 to 3.0 μm; yet it became nanofiber in the spun fibers. Successful fibers of the PBT/P-CAP blends with an average diameter of 20 μm could be spun, where the tensile strength and elongation at break were in the range of 0.6−0.7 g/denier and 12−16%, respectively. Finally, the ultra-fine PBT nanofibers with diameters in the range of 50−70 nm were observed after removing the P-CAP matrix with acetone from the fibers, owing to the formation of PBT nanofibers during spinning and orientation processes. This method thus could successfully produce nano-scale PBT fibers with fineness comparable with the nanofibers developed via electrospinning technology.
關聯:	Journal of Polymer Research 25(4), p.25:88