    題名: 聚偏二氟乙烯中空纖維膜應用於海水淡化之研究
    其他題名: A study on performance of PVDF hollow fiber in membrane distillation
    作者: 廖一錚;Liao, Yi-Jheng
    貢獻者: 淡江大學化學工程與材料工程學系碩士班
    鄭東文
    關鍵詞: 聚偏二氟乙烯;中空纖維膜;直接接觸式蒸餾;真空式蒸餾;poly(vinylidene fluoride);hollow fiber membrane;Vacuum Membrane Distillation;Direct contact membrane distillation
    日期: 2016
    上傳時間: 2017-08-24 23:49:47 (UTC+8)
    摘要: 本研究以實驗室合成之聚偏二氟乙烯(poly(vinylidene fluoride), PVDF)中空纖維膜組裝之模組進行直接接觸式薄膜蒸餾(direct contact membrane distillation)及真空式薄膜蒸餾(vacuum membrane distillation)實驗，進料溶液為3.5 wt%之鹽水溶液，操作參數為進料溫度(50~70 oC)及進料速率(0.2~0.5 L/min)，真空式薄膜蒸餾其真空度為持在8 kPa，直接接觸式薄膜蒸餾之冷水側溫度為13 oC及進料速率0.4 L/min。
    製備中空纖維膜的條件為改變芯液之組成，其中共4種條件分別為20、30、40、60 wt%磷酸三乙酯(TEP)水溶液，藉由硬性換成軟性的方式來改善中空纖維膜內表面結構。從SEM解析得知隨著磷酸三乙酯(TEP)在芯液的比例增加薄膜內表面皮層結構不易形成，且大孔洞數變多。
    真空式及直接接觸式薄膜蒸餾操作中，提高進料溫度能明顯增加滲透通量，但極化現象也較嚴重，此外薄膜於真空式薄膜蒸餾會有fouling現象，造成氯化鈉顆粒析出於殼測薄膜表面，此種現象會造成薄膜之有效面積減少，降低純水通量。增加進料流率對於滲透通量之提升較不顯著，但對於高溫進料操作之溫度極化現象具有較明顯改善效果。
    其結果顯示隨著芯液中TEP wt%的比例增加，所製成的薄膜在直接接觸式薄膜蒸餾有較高的通量，在真空式薄膜蒸餾中更加明顯。孔洞較大的薄膜對於進料溫度及速率的增加在通量的提升效果高於小孔洞之薄膜。此外短模組在真空及直接接觸式薄膜蒸餾操作中的滲透通量都明顯高於長模組。
    In this study, laboratory made poly(vinylidene fluoride), PVDF, hollow fiber membranes were used in vacuum and direct contact membrane distillation of saline solution. The feed solution was 3.5 wt% NaCl solution, the operating parameters included feed temperature (50 ~ 60 oC), feed rate (0.2 ~ 0.5 L / min), the vacuum pressure in the permeate side was controlled at 8 kPa for vacuum membrane distillation, and cooling water controlled at 13 oC with rate 0.4 L / min for direct contact membrane distillation.
    The hollow fiber membranes were prepared by varying the composition of the bore liquid. There were four conditions, which 20、30、40、60 wt% triethylphosphate (TEP) solution. The inner skin of the hollow fiber membrane was improved by changed the bore liquid from hard coagulation (water bath) to soft coagulation. Analysis the structure by SEM morphology, which membrane have large pore size in the inner surface by increasing the weight percent of TEP in bore liquid.
    In the vacuum and direct contact membrane distillation experiment, raising the temperature of the feed can significantly increase the flux, but the polarization phenomena become more serious. In addition, the membrane surface will have fouling phenomenon that NaCl was separated out to the shell side membrane surface in vacuum membrane distillation. This situation will cause decrease the effective area of the membrane and reduce the flux. Increasing feed flow rate has a finite effect on increasing the flux, but the temperature polarization phenomenon can be reduced by the feed flow rate as higher feed temperature.
    The experimental results showed the higher flux performance on direct contact membrane distillation which prepared by higher weigh percent of TEP bore liquid solution obviously in the vacuum membrane distillation. The large pore size membrane flux which increased by higher inlet temperature more obvious then the small one. Furthermore, the short module have higher flux then long module in the same inlet condition.
    顯示於類別:[化學工程與材料工程學系暨研究所] 學位論文