Microstructural Analysis and Sintering of Precipitated Silver Chloride Films

淡江大學機構典藏 > 工學院 > 機械與機電工程學系暨研究所 > 期刊論文 > Item 987654321/108686

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/108686

題名:	Microstructural Analysis and Sintering of Precipitated Silver Chloride Films
作者:	Cheng-Chih Shih;C.B. Lin
關鍵詞:	Silver chloride films;Precipitation;Sodium chloride;Silver nitrate;Morphology;Growth;mechanisms
日期:	2016-12-01
上傳時間:	2016-12-03 02:10:35 (UTC+8)
出版者:	Springer US
摘要:	Silver chloride thin film with high specific surface area was synthesized through heterogeneous precipitation reaction by adding sodium chloride solution on top of frozen silver nitrate solution. The bottom surface (contact with frozen silver nitrate solution) morphology of the silver chloride film comprises numerous porous stick structures. The top surface (contact with sodium chloride solution) consists of equiaxed grains, and columnar grains are observed in the cross section. The effects of sintering temperature and time on the morphology and grain growth mechanisms of the film are also investigated. The grain growth mechanism belongs to an anomalous diffusion involving case I diffusion and case II diffusion. Interface diffusion occurs only at high sintering temperatures, while diffusion-controlled growth dominates at low sintering temperatures. The activation energy of the interface-controlled growth is 50 kJ/mol, while that of diffusion-controlled growth is 10 kJ/mol.
關聯:	Metallography, Microstructure, and Analysis 5(6), p.493-504
DOI:	10.1007/s13632-016-0317-6
顯示於類別:	[機械與機電工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	240	檢視/開啟
Microstructural Analysis and Sintering of Precipitated Silver.pdf		2647Kb	Adobe PDF	2	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章