    題名: 黏彈性對塑膠射出光學鏡片之光學品質的影響
    作者: Lai, De-Lung;Lin, Gwo-Geng;Huang, Chao-Tsai (CT);Wang, Chen-Chieh;Chang, Yuan-Jung;Chang, Rong-Yeu
    關鍵詞: 流變學;黏彈性;雙折射;Cross model;White-Metzner model
    日期: 2016-01-30
    上傳時間: 2016-04-27 11:24:48 (UTC+8)
    摘要: In modern life, polymeric optical lens has been utilized in many electronic devices, such as camera, mobile phone, tablet, and other optical devices. Although hundred million lenses are produced annually for these devices, the quality is the key to the main suppliers. Indeed, the optical quality can be affected by the geometric features and/or the optical birefringence. However, how the material’s viscoelasticity influences the optical features is still not fully understood yet. In this study, we have investigated the viscoelastic effects on the optical property of a lens made of Zeonex COP 480R material by the traditional injection molding, simulated with n = 0.4 and * = 217,000 Pa in the Cross model. Results show that if the power-law index (n) was varied from 0.1 to 0.6, the total fringed order has no significant difference, but the fringed patterns were varying dominantly in the perpendicular direction, instead of the flow direction for the case at n = 0.4.
    This situation was matched with the distribution of the flow-induced residual stresses. Moreover, if the * in the Cross model was varied from 100,000 Pa to 300,000 Pa, the total fringed patterns were apparently changing from being dominated in the flow direction to being in the direction perpendicular to the flow. The influenced width of the fringed patterns was almost linearly increased with the increasing *. The results can be applied as some guideline for either the further material modifications or the new material developments.
    關聯: 第39屆高分子研討會論文集光碟 OC-01
    顯示於類別:[化學工程與材料工程學系暨研究所] 會議論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html全文0KbHTML176檢視/開啟
    index.html議程0KbHTML155檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋