Thermal analyses of dye disperse red 1 grafted onto silica nanoparticles

doi:10.1007/s11998-015-9670-7

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 會議論文 > Item 987654321/106795

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/106795

題名:	Thermal analyses of dye disperse red 1 grafted onto silica nanoparticles
作者:	Chao-Ching Chang, Feng-Hsi Huang, Zi-Min Lin, Liao-Ping Cheng
關鍵詞:	Dye;Silica;Thermal behavior;Thermal stability;Crystallinity;Degradation
日期:	2014-09-25
上傳時間:	2016-04-27 11:24:16 (UTC+8)
摘要:	Dye-grafted silica nanoparticles (GSiO2) were synthesized via a dual-step process involving, first, attachment of the organic dye Disperse Red 1 (DR1) to the coupling agent, 3-isocyanatopropyltriethoxysilane, by means of urethane bonds, and then grafting of the silylated-DR1 onto silica nanoparticles (~6 nm) prepared by hydrolysis and condensation of tetraethoxysilane in a sol–gel process. Dye-adsorbed silica nanoparticles (DSiO2) were also prepared for comparison, for which DR1 was bound only physically to silica instead of covalent bonds. The thermal behaviors of the formed GSiO2 and DSiO2 were examined by means of differential scanning calorimetry and thermal gravimetric analysis. The results showed that both the particle size and silica content have significant effects on the thermal behaviors of the dye-adsorbed and dye-grafted silica. Moreover, crystalline DR1 lost significantly its crystallinity after being adsorbed on silica, and became virtually amorphous after being grafted onto silica. The formed particles were UV-cured with a multifunctional acrylic monomer to yield color coatings on glass substrates. UV–visible spectra indicated that brightness and color saturation of the coating comprising GSiO2 could be maintained better than that comprising DSiO2 after heat treatment at 280°C.
關聯:	Journal of Coatings Technology and Research 12(4), pp.731-738
DOI:	10.1007/s11998-015-9670-7
顯示於類別:	[化學工程與材料工程學系暨研究所] 會議論文