    题名: Thermal analyses of dye disperse red 1 grafted onto silica nanoparticles
    作者: Chao-Ching Chang, Feng-Hsi Huang, Zi-Min Lin, Liao-Ping Cheng
    关键词: Dye;Silica;Thermal behavior;Thermal stability;Crystallinity;Degradation
    日期: 2014-09-25
    上传时间: 2016-04-27 11:24:16 (UTC+8)
    摘要: Dye-grafted silica nanoparticles (GSiO2) were synthesized via a dual-step process involving, first, attachment of the organic dye Disperse Red 1 (DR1) to the coupling agent, 3-isocyanatopropyltriethoxysilane, by means of urethane bonds, and then grafting of the silylated-DR1 onto silica nanoparticles (~6 nm) prepared by hydrolysis and condensation of tetraethoxysilane in a sol–gel process. Dye-adsorbed silica nanoparticles (DSiO2) were also prepared for comparison, for which DR1 was bound only physically to silica instead of covalent bonds. The thermal behaviors of the formed GSiO2 and DSiO2 were examined by means of differential scanning calorimetry and thermal gravimetric analysis. The results showed that both the particle size and silica content have significant effects on the thermal behaviors of the dye-adsorbed and dye-grafted silica. Moreover, crystalline DR1 lost significantly its crystallinity after being adsorbed on silica, and became virtually amorphous after being grafted onto silica. The formed particles were UV-cured with a multifunctional acrylic monomer to yield color coatings on glass substrates. UV–visible spectra indicated that brightness and color saturation of the coating comprising GSiO2 could be maintained better than that comprising DSiO2 after heat treatment at 280°C.
    關聯: Journal of Coatings Technology and Research 12(4), pp.731-738
    DOI: 10.1007/s11998-015-9670-7
    显示于类别:[化學工程與材料工程學系暨研究所] 會議論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML112检视/开启

    在機構典藏中所有的数据项都受到原著作权保护.

    TAIR相关文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回馈