Effect of Curing Temperature on Properties and Solvent Welding Strength of Ovalbumin

淡江大學機構典藏 > 工學院 > 機械與機電工程學系暨研究所 > 期刊論文 > Item 987654321/106092

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/106092

题名:	Effect of Curing Temperature on Properties and Solvent Welding Strength of Ovalbumin
作者:	Lin, Ching-bin
关键词:	ovalbumin;crosslinking;curing;tensile;joint strength;solvent welding
日期:	2011-10-26
上传时间:	2016-04-22 13:19:35 (UTC+8)
摘要:	Effect of curing temperature on properties of ovalbumin has been investigated. Functional basis, crosslinking degree, tensile strength, and hardness increases with rising curing temperature. The increase of visible transmittance and the decrease of absorption accompany with increasing wavelength. The absorptive peak shows at 440–450 nm and the wavelength of the absorptive peak increases with the rising curing temperature. The relationship of joint strength with solvent welded joints of ovalbumin to their microstructure is also investigated. Ovalbumin can promote joint strength after the treatment of distilled water and curing. Comparing joint strength with fracture morphology, the smoother fracture surface morphology is related to the maximum tensile and shear joint strength, respectively. The joint strength is increasing with curing temperature and compressive stress, and the joint strength of treatment with 150°C curing temperature and 0.12 kgf/mm2 compressive stresses are larger than its original tensile fracture strength of cured ovalbumin at same curing temperature.
關聯:	Journal of Applied Polymer Science 124(3),　p.2144-2153
DOI:	10.1002/app.35311
显示于类别:	[機械與機電工程學系暨研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	222	检视/开启
Lin_et_al-2012-Journal_of_Applied_Polymer_Science (1).pdf		1971Kb	Adobe PDF	2	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章