Effect of chemical roughening on adhesive strength of aluminum flake doped ABS/PC overmoulded with SEBS.

淡江大學機構典藏 > 工學院 > 機械與機電工程學系暨研究所 > 期刊論文 > Item 987654321/106087

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/106087

題名:	Effect of chemical roughening on adhesive strength of aluminum flake doped ABS/PC overmoulded with SEBS.
作者:	Lin, C.B.;Chang, Z.C.;Hsueh, H.-C.;Wang, W.-C.
關鍵詞:	Aluminium flake;Metallised plastics;Chemical roughening;Adhesive strength
日期:	2011-01-13
上傳時間:	2016-04-22 13:19:24 (UTC+8)
出版者:	Taylor & Francis
摘要:	Acrylonitrile butadiene styrene+20 wt-% polycarbonate (PC)/27 wt-% aluminium flake metallised plastics were immersed in aqueous H2SO4 for chemical roughening. The adhesive strengths of the metallised plastics that were roughened at various corrosion temperatures (30–90°C) for various times (10–30 min) with styrene–ethylene–butene–styrene at various melting temperatures (180–220°C) were investigated. Experimental results indicate that the aluminium flakes reduce the activation energy of the metallised plastics in aqueous H2SO4 at 30–70°C. The roughness and the weight rate of the roughened metallised plastics increase with corrosion temperature and time. Corrosion at 70°C for 10 min yields the largest effective adhesive area and adhesive strength. The adhesive strength increases with the melting temperature of styrene–ethylene–butene–styrene.
關聯:	Plastics, Rubber & Composites: Macromolecular Engineering 41(8), p.350-357
DOI:	10.1179/1743289811Y.0000000034
顯示於類別:	[機械與機電工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	296	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章