Structural modification of nanocrystalline diamond films via positive/negative bias enhanced nucleation and growth processes for improving their electron field emission properties

doi:10.1063/1.4921875

淡江大學機構典藏 > 理學院 > 物理學系暨研究所 > 期刊論文 > Item 987654321/104599

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/104599

題名:	Structural modification of nanocrystalline diamond films via positive/negative bias enhanced nucleation and growth processes for improving their electron field emission properties
作者:	Saravanan, A.;Huang, B. R.;Sankaran, K. J.;Keiser, G.;Kurian, J.;Tai, N. H.;Lin, I. N.
日期:	2015-05-02
上傳時間:	2016-01-06 11:04:26 (UTC+8)
摘要:	Electron field emission (EFE) properties of nanocrystalline diamond (NCD) films synthesized by the bias-enhanced growth (beg) process under different bias voltages were investigated. The induction of the nanographitic phases is presumed to be the prime factor in enhancing the EFE properties of negative biased NCD films. Transmission electron microscopic investigations reveal that a negative bias voltage of −300 V increases the rate of growth for NCD films with the size of the grains changing from nano to ultranano size. This effect also is accompanied by the induction of nanographitic filaments in the grain boundaries of the films. The turn-on field (E 0) for the EFE process then effectively gets reduced. The EFE process of the beg-NCD−300V films can be turned on at E 0 = 3.86 V/μm, and the EFE current density achieved is 1.49 mA/cm2 at an applied field of 7.85 V/μm. On the other hand, though a positive-bias beg process (+200 V) results in the reduction of grain size, it does not induce sufficient nanographitic phases to lower the E 0 value of the EFE process. Moreover, the optical emission spectroscopic investigation indicates that one of the primary causes that changes the granular structure of the NCD films is the increase in the proportion of C2 and CH species induced in the growing plasma. The polarity of the bias voltage is of less importance in the microstructural evolution of the films.
關聯:	Journal of Applied Physics 117(21), 215307
DOI:	10.1063/1.4921875
顯示於類別:	[物理學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	190	檢視/開啟
Structural modification of nanocrystalline diamond films via positive negative bias enhanced nucleation and growth processes for improving their electron field emission properties.pdf		4272Kb	Adobe PDF	1	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....