    題名: Correlation Between Electrochromism and Electronic Structures of Tungsten Oxide Films
    作者: Limaye, M. V.;Chen, J. S.;Singh, S. B.;Shao, Y. C.;Wang, Y. F.;Pao, C. W.;Tsai, H. M.;Lee, J. F.;Lin, H. J.;Chiou, J. W.;Yang, M. C.;Wu, W. T.;Chen, J. S.;Wu, J. J.;Tsai, M. H.;Pong, W. F.
    日期: 2013-12-02
    上傳時間: 2016-01-06 11:03:58 (UTC+8)
    摘要: The in-situ X-ray absorption spectroscopy of three tungsten oxide films was performed to study the electronic and atomic structures following repeated cycles of coloration and bleaching processes. The transparent tungsten oxide films become deep blue upon intercalation of Li+ ions in the WO6 octahedra when an external electrical bias was applied. These films reverted to transparent when a reverse external electrical bias was applied. W L3-edge X-ray absorption near-edge structure (XANES) measurements of the nanocrystalline and crystalline tungsten oxide films revealed that the intensity of the white-line feature decreases after coloration and recoverably increases after bleaching owing to the filling and unfilling of the W 5d–O 2p conduction band states. The second derivative of the W L3-edge XANES spectra indicated an increase in structural disordering following repeated cycles of coloration and bleaching. However, the extended X-ray absorption fine structure analysis showed that the nearest-neighbor W–O bond distances in the samples overall remain unchanged by coloration and bleaching. The nanocrystalline tungsten oxide film exhibited more effective recovery (∼97% after first cycle) of the electronic structures than the other two crystalline samples in terms of the filling and unfilling of the W 5d–O 2p conduction band states after repeated coloration and bleaching. These results show that the nanocrystalline tungsten oxide sample has superior electrochromic properties to the crystalline samples.
    關聯: RSC Advances 4, pp.5036-5046
    DOI: 10.1039/C3RA45421E
    顯示於類別:[物理學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    Correlation Between Electrochromism and Electronic Structures of Tungsten Oxide Films.pdf1535KbAdobe PDF3檢視/開啟
    index.html0KbHTML325檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋