    題名: Synthesis of Core-shell Nano-particulate Polyelectrolyte
    作者: Lin, Dar-Jong;Lu, Yuan-Pei
    貢獻者: 淡江大學化學工程與材料工程學系
    關鍵詞: polyelectrolyte;core-shell
    日期: 2015-05-20
    上傳時間: 2015-06-17 16:36:40 (UTC+8)
    出版者: Elsvier
    摘要: The nano-particle consists two principal constituent monomers, of which one is electrolyte with sulfonic acid group: 2-Acrylamido-2-methyl-1-propane sulfonic acid (AMPS), and the other is multi-vinyl: 1,1,1-Trimethylolpropane triacrylate (TMPTA). Synthesis was found to be composed of two stages. The early precipitation polymerization leads to the formation of nuclei, which grow gradually to particulate core of size about 10 to 20 nm at least. Subsequent emulsion-assisted polymerization permits the formation of electrolytic shell part over the core. The reaction control was facilitated through the photo-initiation mechanism at ambient temperature. The particle composition was revealed by FTIR, and the characterization of particle size was effectuated by both DLS and FESEM. IR spectrum as shown below confirms that TMTPA (n ̅ = 1732 cm-1, ester C=O) and AMPS (n ̅ = 1040 cm-1, symmetric stretching sulfonic SO3 hydrated) both constitute significantly the particle. The particle size was measured to be about 20~30 nm by FESEM as indicated in the micrograph below, whereas, about 60~70 nm by DLS. This large difference, between dry vacuum state and aqueous solution state, reveals the fact that the hydrodynamic volume of particle may represent the tremendous swelling of polyelectrolyte shell part in aqueous solution. The quantitative composition of particle will be pursued by elemental analysis, EDS, XPS. And the morphologic core-shell structure will be characterized by TEM and SAXS.
    顯示於類別:[化學工程與材料工程學系暨研究所] 會議論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    Frontiers in Polymer Science_Dar-Jong Lin.docx431KbMicrosoft Word181檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋