    題名: Flammability and tensile properties of polylactide nanocomposites with short carbon fibers
    作者: Cheng, K.-C., Lin, Y.-H., Guo, W., Chuang, T.-H.;Chang, S.-C.;Wang, S.-F.;Don, T.-M.
    貢獻者: 淡江大學化學工程與材料工程學系
    日期: 2015-02
    上傳時間: 2015-03-11 20:43:37 (UTC+8)
    出版者: New York: Springer New York LLC
    摘要: Nanocomposites of polylactide (PLA) with aluminum hydroxide (ATH), short carbon fibers (CF), and montmorillonite (MMT) were prepared via direct melt blending. The exfoliated and intercalated clay structures with some aggregations in the PLA matrix were observed. The tensile strength and elongation at break of the PLA composite caused by the high content of the retardant ATH were improved by adding modified MMT and CF to replace a portion of ATH in the PLA matrix. The thermal degradation temperatures and char residue of the PLA/ATH/MMT/CF nanocomposites as determined by thermogravimetric analysis were higher than without MMT. Furthermore, a novel method was proposed to analyze the flammability of composite using an infrared camera, which could capture the apparent thermal image of the sample during UL 94 V test. It was found that, with addition of the MMT and short CF, a more effective insulation layer could be formed on the ablating surface of the PLA/ATH composite, and the high thermal conductivity of the CF might increase the release rate of heat from the surface composite during burn, thus the PLA/ATH/MMT nanocomposite containing short carbon fibers having a V-0 rating without flaming dripping could be obtained.
    關聯: Journal of Materials Science 50(4), pp.1605-1612
    顯示於類別:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    2015 J mater sci Flammability and tensile properties of polylactide nanocomposites.pdf1012KbAdobe PDF274檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋