    题名: Crack Filling of Cover Glasses by Sol-gel Coatings
    作者: Ma, Kung-Jeng;Chien, Hsi-Hsin;Huang, Su-Wei;Chen, Shi-Chang;Chao, Choung-Lii
    贡献者: 淡江大學機械與機電工程學系
    关键词: Cover Glass;Crack Repair;Edge Strengthening;Sol-Gel Coating
    日期: 2013-09
    上传时间: 2015-03-02 23:09:37 (UTC+8)
    出版者: TTP
    Pfaffikon: Scientific.Net
    摘要: Strengthening of glass sheets through the process of ion exchange have been widely used in thinner cover glass for smart phone. The compressive stress improves the ability of the glass surface to withstand damage from mechanical impact. However, the presence of the damage resistant layer makes conventional mechanical and laser cutting of the ion-exchanged glass difficult. Normally, the cutting process will lead to spontaneous glass sheet breakage or shattering. Even successful in some samples, the underlying central tension is exposed on the edge, and the mechanical strength and durability of this edge is degraded. The repair of edge cracks becomes an extremely important issue for the development of single glass based smart phone. The ion exchanged glass plates (Corning IOX-FS) with a thickness of 0.7 mm were selected as the substrate materials. After cutting ion exchanged glass by high penetration diamond scribing wheels, the edge of glass plates can be protected or strengthened with silica sol using roll coating process. It was observed that the strength could be improved achieving 210 % compared to the strength of uncoated glass sheets. The sol-gel coating could improve the strength of the glass mainly by the mechanisms of filling in edge flaws or blunting crack tips. The effects of silica sol and processing parameters of roll coating process on the cracks filling effects were investigated.
    關聯: Advanced Materials Research 797, pp.700-705
    DOI: 10.4028/www.scientific.net/AMR.797.700
    显示于类别:[機械與機電工程學系暨研究所] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML271检视/开启

    在機構典藏中所有的数据项都受到原著作权保护.

    TAIR相关文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回馈