    題名: The microstructural evolution of ultrananocrystalline diamond films due to P ion implantation process—the annealing effect
    作者: Lin, Sheng-Chang;Yeh, Chien-Jui;Joji Kurian;Dong, Chung-Li;Huan Niu;Leou, Keh-Chyang;Lin, I.-Nan;林諭男
    貢獻者: 淡江大學物理學系
    日期: 2014-01-01
    上傳時間: 2015-02-03 16:39:01 (UTC+8)
    出版者: College Park: American Institute of Physics
    摘要: The microstructural evolution of UNCD films which are P-ion implanted and annealed at 600 °C (or 800 °C) is systematically investigated. The difference of interaction that the UNCD content undergoes along the trajectory of the incident P-ions is reflected in the alteration of the granular structure. In regions where the P-ions reside, the “interacting zone,” which is found at about 300 nm beneath the surface of the films, coalescence of diamond grains occurs inducing nano-graphitic clusters. The annealing at 600 °C (or 800 °C) heals the defects and, in some cases, forms interconnected graphitic filaments that result in the decrease in surface resistance. However, the annealing at 600 °C (800 °C) induces marked UNCD-to-Si layers interaction. This interaction due to the annealing processes hinders the electron transport across the interface and degrades the electron field emission properties of the UNCD films. These microstructural evolution processes very well account for the phenomenon elaborating that, in spite of enhanced conductivity of the UNCD films along the film's surface due to the P-ion implantation and annealing processes, the electron field emission properties for these UNCD films do not improve.
    關聯: Journal of Applied Physics 116, 183701(11pages)
    DOI: 10.1063/1.4901333
    顯示於類別:[物理學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML99檢視/開啟
    The microstructural evolution of ultrananocrystalline diamond films due to P ion implantation process—the annealing effect.pdf6379KbAdobe PDF0檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋